设计了一步等温和两步等温Q&P处理，通过改变淬火温度和等温温度使30CrMnSiA钢获得了不同含量一次马氏体(PM)、残留奥氏体(RA)、二次马氏体(FM)及贝氏体(BF)的多相微观组织。采用X射线衍射(XRD)、电子背散射衍射(EBSD)技术和透射电镜(TEM)等分析了Q&P处理对试验钢组织和力学性能的影响，并分析了热处理工艺影响RA含量、形态和C浓度的微观机制。结果表明：Q&P工艺中的淬火温度和等温温度决定了各相的含量和特性，高的等温温度有利于提升试验钢的拉伸塑性，而残留奥氏体的含量和碳浓度能够显著影响试验钢的伸长率、强塑积和屈服强度；330℃是一步等温和两步等温处理的最佳淬火温度，该温度下高的RA的含量及C浓度能够显著提升30CrMnSiA钢的伸长率、强塑积和屈服强度。与一步等温Q&P处理比较，两步等温Q&P处理可以提高组织中的RA含量，并能显著降低FM含量，这有助于提升30CrMnSiA钢的力学性能。
Abstract：A one-step isothermal and two-step isothermal Q&P treatment was designed, and the multiphase microstructure of 30CrMnSiA steel with different contents of primary martensite(PM), retained austenite(RA), secondary martensite(FM) and bainite(BF) was obtained by changing the quenching temperature and isothermal temperature. The effects of Q&P treatment on microstructure and mechanical properties of the experimental steel were analyzed by means of X-ray diffraction(XRD), electron backscatter diffraction(EBSD) technique and transmission electron microscopy(TEM). The micro mechanisms by which the heat treatment process affects the RA content, morphology and C concentration were also analyzed. The results show that the quenching temperature and isothermal temperature in the Q&P process determine the content and characteristics of each phase. A high isothermal temperature is beneficial for improving the tensile plasticity of the experimental steel, while the content of retained austenite and carbon concentration can significantly affect the elongation, product of strength and elongation, and yield strength of the experimental steel. 330 ℃ is the optimal quenching temperature for one-step and two-step isothermal treatment. At this temperature, high RA content and C concentration can significantly improve the elongation, product of strength and elongation, and yield strength of the 30CrMnSiA steel. Compared with one-step isothermal Q&P treatment, two-step isothermal Q&P treatment can increase the RA content in the microstructure and significantly reduce the FM content, which helps to improve the mechanical properties of the 30CrMnSiA steel.
[1] 何方.Q&P钢连续退火工艺的组织性能调控技术研究[D].北京：钢铁研究总院，2021.HE Fang.Study on microstructure and mechanical properties control technology of Q&P steel under continuous annealing process[D].Beijing:Central Iron & Steel Research Institute,2021.
[2] 蒯振，陈银莉，庄宝潼，等.低碳Si-Mn系Q&P钢两相区的退火热处理工艺[J].材料热处理学报，2012,33(12):88-93.KUAI Zhen,CHEN Yin-li,ZHUANG Bao-tong,et al.Quenching and partitioning (Q&P) process in two-phase region of a low carbon Si-Mn steel[J].Transactions of Materials and Heat Treatment,2012,33(12):88-93.
[3] Clarke A J,Speer J G,Miller M K,et al.Carbon partitioning to austenite from martensite or bainite during the quench and partition (Q&P) process:A critical assessment[J].Acta Materialia,2008,56(1):16-22.
[4] Chen S,Hu J,Shan L,et al.Characteristics of bainitic transformation and its effects on the mechanical properties in quenching and partitioning steels[J].Materials Science and Engineering A,2021,803:140706.
[5] Li H Y,Lu X W,Wu X C,et al.Bainitic transformation during the two-step quenching and partitioning process in a medium carbon steel containing silicon[J].Materials Science and Engineering A,2010,527(23):6255-6259.
[6] Samanta S,Biswas P,Giri S,et al.Formation of bainite below the Ms temperature:Kinetics and crystallography[J].Acta Materialia,2016,105:390-403.
[7] 黄峰.淬火-配分钢的组织调控与力学性能研究[D].上海：上海交通大学，2016.HUANG Feng.Investigation on the microstructural control and mechanical properties of quenched & partitioning steels[D].Shanghai:Shanghai Jiao Tong University,2016.
[8] 张君.低碳高强度Q&P钢的热处理工艺及变形机制研究[D].沈阳：东北大学，2015.ZHANG Jun.Research on heat treatment process and deformation mechanism of low carbon high strength Q&P steel[D].Shengyang:Northeastern University,2015.
[9] Qian L H,Li Z,Wang T L,et al.Roles of pre-formed martensite in below-Ms bainite formation,microstructure,strain partitioning and impact absorption energies of low-carbon bainitic steel[J].Journal of Materials Science & Technology,2022,96:69-84.
[10] Sohrabi M J,Mirzadeh H,Sadeghpour S,et al.Grain size dependent mechanical behavior and TRIP effect in a metastable austenitic stainless steel[J].International Journal of Plasticity,2023,160:103502.
[11] 刘伟，闫泰起，孙兵兵，等.30CrMnSiA高强钢拉杆激光熔覆修复[J].航空材料学报，2022,42(3):12-20.LIU Wei,YAN Tai-qi,SUN Bing-bing,et al.Repair of 30CrMnSiA high strength steel pull rod by laser cladding[J].Journal of Aeronautical Materials,2022,42(3):12-20.
[12] Baek M S,Kim K S,Park T W,et al.Quantitative phase analysis of martensite-bainite steel using EBSD and its microstructure,tensile and high-cycle fatigue behaviors[J].Materials Science and Engineering A,2020,785:139375.
[13] Wang X L,Ma X P,Wang Z Q,et al.Carbon microalloying effect of base material on variant selection in coarse grained heat affected zone of X80 pipeline steel[J].Materials Characterization,2019,149:26-33.
[14] Miyamoto G,Takayama N,Furuhara T.Accurate measurement of the orientation relationship of lath martensite and bainite by electron backscatter diffraction analysis[J].Scripta Materialia,2009,60:1113-1116.
[15] Wu B B,Wang Z Q,Wang X L,et al.Toughening of martensite matrix in high strength low alloy steel:Regulation of variant pairs[J].Materials Science and Engineering A,2019,759:430-436.
[16] Wu B B,Wang Z Q,Yu Y S,et al.Thermodynamic basis of twin-related variant pair in high strength low alloy steel[J].Scripta Materialia,2019,170:43-47.
[17] Wang X L,Wang Z Q,Ma X P,et al.Analysis of impact toughness scatter in simulated coarse-grained HAZ of E550 grade offshore engineering steel from the aspect of crystallographic structure[J].Materials Characterization,2018,140:312-319.
[18] Zhao L,Qian L,Meng J,et al.Below-Ms austempering to obtain refined bainitic structure and enhanced mechanical properties in low-C high-Si/Al steels[J].Scripta Materialia,2016,112:96-100.
[19] Zinsaz-Borujerdi A,Zarei-Hanzaki A,Abedi H R,et al.Room temperature mechanical properties and microstructure of a low alloyed TRIP-assisted steel subjected to one-step and two-step quenching and partitioning process[J].Materials Science and Engineering A,2018,725:341-349.
[20] Chen K,Li H,Jiang Z,et al.Multiphase microstructure formation and its effect on fracture behavior of medium carbon high silicon high strength steel[J].Journal of Materials Science & Technology,2021,72:81-92.
[21] Wang Y,Xu Y,Zhang T,et al.Effects of quenching temperature on bainite transformation,retained austenite and mechanical properties of hot-galvanized Q&P steel[J].Materials Science and Engineering A,2021,822:141643.
[22] Zhou C,Ye Q B,Zhao T,et al.Strengthening and toughening mechanisms in Ni-alloyed steel:Enhancing the integral stability of retained austenite[J].Materials Science and Engineering A,2022,852:143703.
[23] 陈连生，张家豪，刘麟，等.连续退火均热时间对Q&P钢Mn元素分布及加工硬化的影响[J].材料热处理学报，2022,43(11):111-120.CHEN Lian-sheng,ZHANG Jia-hao,LIU Lin,et al.Effect of continual annealing soaking time on Mn element distribution and work hardening of Q&P steel[J].Transactions of Materials and Heat Treatment,2022,43(11):111-120.
[24] De Knijf D,Petrov R,F?jer C,et al.Effect of fresh martensite on the stability of retained austenite in quenching and partitioning steel[J].Materials Science and Engineering A,2014,615:107-115.
[25] Liu L,He B B,Cheng G J,et al.Optimum properties of quenching and partitioning steels achieved by balancing fraction and stability of retained austenite[J].Scripta Materialia,2018,150:1-6.
基本信息:
DOI：10.13289/j.issn.1009-6264.2023-0395
中图分类号:TG142.1
引用信息:
[1]冀宣名,王礼榕,杨明,等.一步等温和两步等温处理对30CrMnSiA钢力学性能的影响[J],2024,45(05):122-134.DOI:10.13289/j.issn.1009-6264.2023-0395.
基金信息:
贵州省自然科学基金重点项目([2020]1Z046);; 贵州省科技支撑计划一般项目([2022]050)