采用内氧化法制备了Cu/Cr2O3弥散强化铜基复合材料,并利用SEM、TEM等分析手段对其性能和微观结构进行了分析。实验结果表明:随着内氧化时间和温度的增加,内氧化层深逐渐增大;随变形量的增加,试样硬度和抗拉强度逐渐升高,导电率略有降低;微观组织分析表明,在铜基体上弥散分布着大量细小均匀的Cr2O3颗粒,其粒径为520nm,颗粒间距为2050nm。
Abstract：Cu/Cr2O3 composite was prepared by internal oxidation.The properties and microstructure of the composite were investigates by means of SEM and TEM.The results indicate that internal oxidation depth of the composite increases gradually with increase of internal oxidation time and temperature.The microhardness and the tensile strength of the composite increase with increasing deformation while the electrical conductivity drops slightly. The investigation of microstructure of the internal oxidation composite shows that a mass of fine Cr2O3 particles is dispersed in the copper matrix,the size of Cr2O3 particles is 5～20nm in diameter and the spatial distance between these particles is 20～50nm.
[1]程建奕,汪明朴.高强高导耐热弥散强化铜合金的研究现[J].材料导报,2004,18(2):38-41.CHENG Jian-yi,WANG Ming-pu.Progress in research on high-strength high-conductivity and high-heat resistance dispersion strengthened copper alloy[J].Materials Review,2004,18(2):38-41.
[2]Groza Joanna.Heat-resistant dispersion-strengthened copper alloys[J].Materials Engineering and Performance,1992,1(1):113-121.
[3]尹志民,张生龙.高强高导铜合金研究热点及发展趋势[J].矿冶工程,2002,22(2):1-5.YIN Zhi-min,ZHANG Sheng-long.Hotspots and developing tendency on high-strength and high-conductivity copper alloys[J].Mining and MetallurgicalEngineering,2002,22(2):1-5.
[4]Naser J,Rieheman W,Ferkel H.Dispersion hardening of metals by nanoscaled ceramic powders[J].Materials Science and Engineering A,1997,234-236:467-469.
[5]于艳梅,杨银仓,李华伦.内氧化制备Cu-Al2O3复合材料新工艺的研究[J].粉末冶金技术,2000,18(4):252-256.YU Yan-mei,YANG Yen-cang,LI Hua-lun.A new method for fabrication of Cu-Al2O3composite by internal oxidation[J].Powder Metallurgy Technology,2000,18(4):252-256.
[6]Srivatsan T S,Narendra N,Troxell J D.Tensile deformation and fracture behavior of an oxide dispersion strengthened copper alloy[J].Materials and Design,2000,21(3):191-198.
[7]程建奕,汪明朴,钟卫佳,等.内氧化法制备的Cu-Al2O3合金的显微组织与性能[J].材料热处理学报,2003,24(1):23-27.CHENG Jian-yi,WANG Ming-pu,ZHONG Wei-jia,et al.Properties and microstructures of Cu-Al2O3alloy produced by internal oxidation[J].Transactionsof Metal Heat Treatment,2003,24(1):23-27.
[8]程建奕,汪明朴,李周,等.Cu-Al2O3纳米弥散强化铜合金的短流程制备工艺及性能[J].材料科学与工艺,2005,13(2):127-130.CHENG Jian-yi,WANG Ming-pu,Li Zhou,et al.A brief manufacturing process and properties of nano-sized Al2O3dispersion strengthened copper alloy[J].Materials Science and Technology,2005,13(2):127-130.
[9]Jerman G A,Anderson I E,Verhoeven J D.Strength and electrical conductivity of deformation-processed Cu-15vol.%Fe alloys produced by powdermetallurgy techniques[J].Metall Trans,1993,24A(1):35-42.
[10]翁宇庆.超细晶钢——钢的组织细化理论与控制技术[M].北京:冶金工业出版社,2003:7-9.
[11]林阳明,宋克兴,李红霞.Al2O3/Cu复合材料强化机理研究[J].热加工工艺,2005,(4):12-14.LIN Yang-ming,SONG Ke-xing,LI Hong-xia.Investigation on strengthened mechanism of Al2O3/Cu composite[J].Hot Working Technology,2005,(4):12-14.
基本信息:
DOI：
中图分类号:TB33
引用信息:
[1]刘勇,田保红,陈卫等.内氧化法制备Cr_2O_3弥散强化铜复合材料[J].材料热处理学报,2008,No.107(05):22-25.
基金信息:
河南省教育厅自然科学基金项目(2006430004);; 河南科技大学基金项目(2007ZY060);; 河南科技大学博士研究启动基金