张春玲,蔡大勇,孔玉婷,杨金凤,廖波

• 1:燕山大学亚稳材料制备技术与科学重点实验室

摘要(Abstract)：

采用Gleeble-3500热模拟试验机研究了Cu-P-Cr-Ni-Mo耐候钢在变形温度700~950℃、变形量70%、应变速率0.01~10 s-1条件下的热变形行为及其热变形的组织演变规律。结果表明,Cu-P-Cr-Ni-Mo耐候钢在700~950℃变形时,峰值应力在低于750℃,高于850℃时随变形温度的升高而降低,而在750~850℃之间随温度升高先降低后升高,在800℃出现极小值。在应变速率和变形量不变的情况下,随着变形温度的降低,组织的细化机制由奥氏体的再结晶细化向铁素体的回复再结晶细化转化,并且铁素体的回复再结晶细化效果更加显著。Cu-P-Cr-Ni-Mo耐候钢在应变速率为1 s-1,变形量为70%的变形条件下,变形温度为775℃时获得的组织细小均匀,铁素体晶粒的平均尺寸约为3μm。

关键词(KeyWords)： 耐候钢;热变形;组织;再结晶;细化

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金(51104130);; 河北省自然科学基金(E2012203137)

作者(Author): 张春玲,蔡大勇,孔玉婷,杨金凤,廖波

DOI: 10.13289/j.issn.1009-6264.2014.02.014

参考文献(References)：

• [1]Erdogan M.Effect of austenite dispersion on phase transformation in dual phase steel[J].Scripta Materialia,2003,48(5):501-506.
• [2]Sun S,Pugh M.Manganese partitioning in dual-phase steel during annealing[J].Materials Science and Engineering A,2000,276(1-2):167-174.
• [3]Seung C H,Kyung S L.Influence of deformation induced ferrite transformation on grain refinement of dual phase steel[J].Materials Science and Engineering A,2002,323(1-2):148-159.
• [4]Süleyman Gündüz.Effect of chemical composition,martensite volume fraction and tempering on tensile behaviour of dual phase steels[J].Materials Letters,2009,63(27):2381-2383.
• [5]Zhang Chunling,Cai Dayong,Liao Bo,et al.Simulation of hot-rolled dual-phase weathering steel 09CuPCrNi[J].Materials Characterization,2005,55(4-5):378-382.
• [6]张春玲,蔡大勇,廖波,等.09CuPCrNiMoNb耐候钢连续冷却转变及热轧双相化的研究[J].材料热处理学报,2004,25(4):37-40.ZHANG Chun-ling,CAI Da-yong,LIAO Bo,et al.Study on continuous cooling transformation and hot rolled dual-phase treatment for 09CuPCrNiMoNb weathering steel[J].Transactions of Materials and Heat Treatment,2004,25(4):37-40.
• [7]Bleck W,Papaefthymiou S,Frehn A.Microstructure and tensile properties in dual phase and TRIP steels[J].Steel Research International,2004,75(10):704-710.
• [8]Adamczyk J,Grajcar A.Structure and mechanical properties of DP-type and TRIP-type sheets obtained after the thermomechanical processing[J].Journal of Materials Processing Technology,2005,162-163(5):267-274.
• [9]Park K T,Lee Y K,Shin D H.Fabrication of ultrafine grained ferrite/martensite dual phase steel by severe plastic deformation[J].ISIJ International,2005,45(5):750-755.
• [10]韩欢庆,葛启录,罗德兴.15钢在双相区控制轧制时的组织变化[J].钢铁研究学报,1998,10(1):20-22.HAN Huan-qing,GE Qi-lu,LUO De-xing.Microstructure in(F+A)region of steel 15 during controlled rolling[J].Journal of Iron and Steel Research,1998,10(1):20-22.
• [11]Huang Y D,Yang W Y,Sun Z Q.Formation of ultrafine grained ferrite in low carbon steel by heavy deformation in ferrite or dual phase region[J].Journal of Materials Processing Technology,2003,134(1):19-25.
• [12]王慧敏,杨忠民,车彦民.普通碳素钢超细晶微观组织的特征分析[J].钢铁研究学报,2006,18(10):45-48.WANG Hui-min,YANG Zhong-min,CHE Yan-min.Ultrafine grain microstructure characteristics of plain low-carbon steel[J].Journal of Iron and Steel Research,2006,18(10):45-48.
• [13]李红英,巫荣海,魏冬冬,等.T23钢的热变形行为[J].材料热处理学报,2013,34(1):96-101.LI Hong-ying,WU Rong-hai,WEI Dong-dong,et al.Thermal deformation behavior of T23 steel[J].Transactions of Materials and Heat Treatment,2013,34(1):96-101.

文章评论(Comment)：