张志宏,薛向欣,冉莲玉,杨合,段培宁

• 1:东北大学材料与冶金学院

摘要(Abstract)：

为考察硼铜低碳钢的腐蚀规律,采用盐雾腐蚀试验和电化学试验研究了硼铜钢的腐蚀行为,结合X射线衍射(XRD)和傅里叶红外光谱(FTIR)对腐蚀产物进行了分析。结果表明:硼与铜复合作用的钢耐蚀性超过铜硼单独添加实验钢,而硼铜分别添加的实验钢耐蚀性相差不明显;3种钢阳极电流密度的变化规律一致,随腐蚀时间延长,阳极电流密度逐渐减小;硼和铜复合添加增强实验钢的阳极极化作用。

关键词(KeyWords)： 盐雾腐蚀试验;硼铜钢;腐蚀速率;极化曲线

Abstract:

Keywords:

基金项目(Foundation): 国家“863”计划项目(2006AA03Z529)

作者(Author): 张志宏,薛向欣,冉莲玉,杨合,段培宁

DOI: 10.13289/j.issn.1009-6264.2013.02.017

参考文献(References)：

• [1]Yamashita M,Shimizu T,Konishi H,et al.Structure and protective performance of atmospheric corrosion product of Fe-Cr alloy film analyzed byMssbauer spectroscopy and with synchrotron radiation X-rays[J].Corrosion Science,2003,45(2):381-394.
• [2]Kimura M,Kihira H,Ishi Y,et al.Corrosion protective mechanism of 3%Ni weathering steel[C]//13th Asian-Pacific Corrosion Control Conference.Osaka University,Japan,2003.
• [3]张全成,王建军,吴建生,等.锈层离子选择性对耐候钢抗海洋大气腐蚀性能的影响[J].金属学报,2001,37(2):193-196.ZHANG Quan-cheng,WANG Jian-jun,WU Jian-sheng,et al.Effect of ion selective property on protective ability of rust layer formed on weatheringsteel exposed in the marine atmosphere[J].Acta Metall Sin,2001,37(2):193-196.
• [4]Choi Yoon-seok,Shim Jac-too,Kim Jun-gu.Corrosion behavior of low alloys steels containing Cr,Co and W in synthetic potable water[J].MaterialsScience and Engineering A,2004,385(1-2):148-156.
• [5]Choi Yoon-seok,Shim Jac-too,Kim Jun-gu.Effects of Cr,Cu,Ni and Ca on the corrosion behavior of low carbon steel in synthetic tap water[J].Journal of alloys and Compounds,2005,391(1-2):162-169.
• [6]Dawson J L,Ferreira M G.Electrochemical studies of the pitting of austenitic stainless steel[J].Corrosion Science,1986,26(12):1009-1026.
• [7]柯伟,董俊华.Mn-Cu钢大气腐蚀锈层演化规律及其耐候性的研究[J].金属学报,2010,46(11):1365-1378.KE Wei,DONG Jun-hua.Study on the rusting evolution and the performance of resisting to atmospheric corrosion for Mn-Cu steel[J].Acta MetallSin,2010,46(11):1365-1378.
• [8]王树涛,杨善武,高克玮,等.低合金耐候钢在含氯离子环境中的耐腐蚀性能[J].材料热处理学报,2008,29(4):170-175.WANG Shu-sheng,YANG Shan-wu,GAO Ke-wei,et al.Corrosion resistance of low alloying weathering steels in environment containing chloride ion[J].Trans Mater Heat Treat,2008,29(4):170-175.

文章评论(Comment)：