摘要(Abstract)：

研制了一种含钛镍基合金,并采用X射线衍射(XRD)、扫描电镜(SEM)及能谱(EDS)等手段研究了其在850℃和950℃熔融硫酸盐中的热腐蚀行为。结果表明,热腐蚀期间,合金发生了氧化、硫化现象,合金表面腐蚀产物层可分为3层,外氧化层以Al2O3、Cr2O3和Cr2O4相为主,中间层为Al2O3相,内层为CrS和Ti2S硫化物层;随腐蚀温度提高合金表面腐蚀层的厚度增加,合金内氧化物区域和内硫化物区域加深。

关键词(KeyWords)： 镍基合金;热腐蚀;熔盐

Abstract:

Keywords:

基金项目(Foundation): 辽宁省博士科研启动基金(20141088)

作者(Author): 杨君宝,邱克强,卢旭东

DOI: 10.13289/j.issn.1009-6264.2015.10.035

参考文献(References)：

• [1]Wang X Y,Li X,Wang F H,et al.Influence of sputtered nanocrystalline coating on oxidation and hot corrosion of a Nickel-based superalloy M951[J].J Mater Sci Technol,2014,30(9):867-868.
• [2]卢旭东,田素贵,王涛,等.溅射Ni Cr Al Y纳米晶涂层在900℃的热腐蚀行为[J].材料热处理学报,2013,34(10):153-154.LU Xu-dong,TIAN Su-gui,WANG Tao,et al.Hot corrosion behaviour of sputtered Ni Cr Al Y nanocrystalline coating in molten sulfate at 900℃[J].Transactions of Materials and Heat Treatment,2013,34(10):153-154.
• [3]卢旭东,田素贵,陈涛,等.高铬镍基合金熔融硫酸盐热腐蚀过程中内氧化和内硫化行为的研究[J].稀有金属材料与工程,2014,43(1):79-81.LU Xu-dong,TIAN Su-gui,CHEN Tao,et al.Internal oxidation and internal sulfuration of Ni-Base alloy with high Cr content during hot corrosion in molten sulfate[J].Rare Metal Materials and Engineering,2014,43(1):79-81.
• [4]Das S,Datta S,Basu D,et al.Hot corrosion of galss coating on nickel based superalloy[J].Ceramics International,2008,34:1217-1218.
• [5]Zhao S Q,Xie X S,Gaylord D S.The oxidation behavior of the new nickel-based superalloy Inconel 740 with and without Na2SO4deposit[J].Surface and Coatings Technology,2004,185:181-182.
• [6]田素贵,卢旭东,孙振东.高Cr镍基合金的高温内氧化和内氮化行为[J].中国有色金属学报,2012,22(2):413-414.TIAN Su-gui,LU Xu-dong,SUN Zhen-dong.Internal oxidation and internal nitridation of Ni-base alloy with high Cr contents during high temperature exposure[J].The Chinese Journal of Nonferrous Metals,2012,22(2):413-414.
• [7]Lu X D,Tian S G,Shui L,et al.Oxidation of behavior of a Ni-based superalloy in air at 800℃[J].Journal of Iron and Steel Research,2010,17:98-100.
• [8]Ren X,Wang F H.High-temperature oxidation and hot-corrosion behaviour of a sputtered Ni Cr Al Y coating with and without aluminizing[J].Surface and Coatings Technology,2006,201:34-35.
• [9]Ren X,Wang F H,Wang X.High-temperature oxidation and hot corrosion behaviors of the Ni Cr-Cr Al coating on a nickel-based superalloy[J].Surface and Coatings Technology,2005,198:429-430.
• [10]Zhang K,Liu M M,Liu S L,et al.Hot corrosion behaviour of a cobalt-base super-alloy K40S with and without Ni Cr Al YSi coating[J].Corrosion Science,2011,53:1995-1996.
• [11]卢旭东,田素贵,于兴福,等.Ni-Cr-Ta-Al-Co-Mo合金在900℃和1000℃的恒温氧化行为[J].材料研究学报,2011,25(4):430-431.LU Xu-dong,TIAN Su-gui,YU Xing-fu,et al.Isothermal oxidation behaviour of Ni-Cr-Ta-Al-Co-Mo alloy at 900℃and 1000℃[J].Chinese Journal of Materials Research,2011,25(4):430-431.
• [12]Li W J,Liu Y,Wang Y,et al.Hot corrosion behavior of Ni-16Cr-x Al based alloys in mixture of Na2SO4-Na Cl at 600℃[J].Transactions of Nonferrous Metals Society of China,2011,21:2623-2624.
• [13]Wang H Y,Zuo D W,Chen G,et al.Hot corrosion behaviour of low Al Ni Co Cr Al Y cladded coatings reinforced by nano-particles on a Ni-base super alloy[J].Corrosion Science,2010,52:3564-3565.
• [14]Zheng L,Zhang M C,Dong J X.Hot corrosion behavior of powder metallurgy Rene95 nickel-based superalloy in molten Na Cl-Na2SO4salts[J].Materials and Design,2011,32:1985-1986.
• [15]Chen L C,Zhang C,Yang Z G.Effect of pre-oxidation on the hot corrosion of Co Ni Cr Al YRe alloy[J].Corrosion Science,2011,53:377-378.
• [16]Han C,Liu Y,Wang Y,et al.Hot corrosion behavior of Ni-x Cr-6.8Al based alloys[J].Transactions of Nonferrous Metals Society of China,2011,21:2355-2356.
• [17]Yu P,Wang W,Wang F H,et al.High-temperature corrosion behavior of sputtered K38 nanocrystalline coatings with and without yttrium addition in molten sulfate at 900℃[J].Surface and Coatings Technology,2011,206:72-73.

文章评论(Comment)：