丁文金,彭同江,陈吉明

• 1:西南科技大学固体废物处理与资源化省部共建教育部重点实验室
• 2:西南科技大学矿物材料及应用研究所

摘要(Abstract)：

以温石棉尾矿、石灰石和石英砂为主要原料,通过不同的热处理过程制备了微晶玻璃。借助DTA、XRD及SEM等分析测试手段,研究了核化和晶化温度对微晶玻璃析晶行为、显微形貌及抗压强度的影响。结果表明:随着热处理温度的升高,微晶玻璃主晶相的种类没有改变,但主晶相衍射峰的强度呈现先增强后减小的趋势。当核化温度为820℃,晶化温度为1050℃时,微晶玻璃样品形成致密的柱状细晶结构,抗压强度达到最大值523 MPa。

关键词(KeyWords)： 温石棉尾矿;微晶玻璃;核化温度;晶化温度

Abstract:

Keywords:

基金项目(Foundation): 固体废物处理与资源化教育部重点实验室资助项目(08zxgp04)

作者(Author): 丁文金,彭同江,陈吉明

DOI: 10.13289/j.issn.1009-6264.2012.05.007

参考文献(References)：

• [1]苏庆平,龙小玲.石棉尾矿的危害及综合利用途径[J].矿产综合利用,2009,32(1):27-31.SU Qing-ping,LONG Xiao-ling.On the approach for comprehensive utilization of asbestos tailing[J].Multipurpose Utilization of Mineral Resources,2009,32(1):27-31.
• [2]栾敬德,李爱民,崔晓波,等.核化和晶化时间对页岩飞灰微晶玻璃性能的影响[J].材料热处理学报,2010,31(7):1-4.LUAN Jing-de,LI Ai-min,CUI Xiao-bo,et al.Effect of nucleation and crystallization time on characteristics of glass ceramics from oil shale fly ash[J].Transactions of Materials and Heat Treatment,2010,31(7):1-4.
• [3]Leroy C,Ferro M C,Monteiro R C C,et al.Production of glass-ceramics from coal ashes[J].Journal of the European Ceramic Society,2001,21:195-202.
• [4]LUAN Jing-de,LI Ai-min,SU Tong,et al.Synthesis of nucleated glass-ceramics using oil shale fly ash[J].Journal of Hazardous Materials,2010,173:427-432.
• [5]ZHAO Tuan,LI Bao-Wei,GAO Zhan-Yong,et al.The utilization of rare earth tailing for the production of glass-ceramics[J].Materials Science andEngineering B,2010,170:22-25.
• [6]杨会智,陈昌平,孙洪巍,等.铝土矿尾矿微晶玻璃研制[J].矿业研究与开发,2007,27(6):48-49.YANG Hui-zhi,CHEN Chang-ping,SU Hong-wei,et al.Study on preparation of glass-ceramics using bauxite tailings[J].Mining Research andDevelopment,2007,27(6):48-49.
• [7]Bernardo E,Castellan R,Hreglich S,et al.Sintered sanidine glass-ceramics from industrial wastes[J].Journal of the European Ceramic Society,2006,26:3335-3341.
• [8]Bernardo E,Castellan R,Hreglich S.Sintered glass-ceramics from mixtures of wastes[J].Ceramics International,2007,33:27-33.
• [9]LIU Cheng-jun,SHI Pei-yang,ZHANG Da-yong,et al.Development of glass ceramics made from ferrous tailings and slag in China[J].Journal of Ironand Steel Research,International,2007,14(2):73-78.
• [10]HUANG Wei-ming,Mats Hillert,WANG Xi-zhen.Thermodynamic assessment of the CaO-MgO-SiO2 system[J].Metallurgical and MaterialsTransactions A.1994,26:1995-2293.
• [11]陈国华.差热分析在微晶玻璃中的应用[J].洛阳工业高等专科学校学报,1995,5(4):5-9.CHEN Guo-hua.Application of DTA in Glass-ceramics[J].Journal of Luoyang Technology College,1995,5(4):5-9.
• [12]Tulyaganov D U,Agathopoulos S,Ventura J M,et al.Synthesis of glass-ceramics in the CaO-MgO-SiO2 system with B2O3,P2O5,Na2O and CaF2additives[J].Journal of the European Ceramic Society,2006,26:1463-1471.
• [13]QIAN Guang-ren,YU Song,ZHANG Can-gang,et al.Diopside-based glass-ceramics from MSW fly ash and bottom ash[J].Waste Management,2006,26:1462-1467.
• [14]冯宗玉,李勇,杨合,等.热处理对油页岩渣微晶玻璃结构的影响[J].材料热处理学报,2008,29(4):29-34.FENG Zong-yu,LI Yong,YANG He,et al.Effect of heat treatment on structure of glass-ceramics prepared with oil shale residue[J].Transactions ofMaterials and Heat Treatment,2008,29(4):29-34.

文章评论(Comment)：