许发红,刘洪喜,张晓伟,蒋业华

• 1:昆明理工大学材料科学与工程学院

摘要(Abstract)：

采用高碳高铬铸铁药芯焊丝,通过自改装的自动搅拌式明弧堆焊机在Q235钢表面堆焊了Fe-Cr-C系耐磨高铬铸铁焊层。借助XRD、SEM、EDS和光学显微镜(OM)分析了堆焊层的物相组成,观察了堆焊层的宏观和微观组织形貌。运用洛氏硬度计和动载冲击磨料磨损试验机测试了堆焊层的表面硬度和磨损性能。结果表明,机械搅拌作用下的明弧堆焊层中裂纹明显减少,焊层内部奥氏体和碳化物更加混乱、细小,局部区域出现了波纹状组织。搅拌作用下的明弧堆焊层最高硬度达57 HRC,相对耐磨性是一般明弧堆焊层的2倍。磨损机制表现为金属的塑性变形和磨料对堆焊层的短距离切削。

关键词(KeyWords)： 明弧堆焊;机械搅拌;高铬铸铁;显微组织;耐磨性能

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金(NSFC61368003)

作者(Author): 许发红,刘洪喜,张晓伟,蒋业华

DOI: 10.13289/j.issn.1009-6264.2015.07.035

参考文献(References)：

• [1]Yang J,Tian J J,Hao F F,et al.Microstructure and wear resistance of the hypereutectic Fe-Cr-C alloy hardfacing metals with different La2O3additives[J].Applied Surface Science,2014,289(1):437-444.
• [2]Dey A,Jha A,Goel U,et al.Failure of high-chromium iron roll in compact strip production mill[J].Case Studies in Engineering Failure Analysis,2013,3(1):186-191.
• [3]Albertin E,Moraes S L.Maximizing wear resistance of balls for grinding of coal[J].Wear,2007,263(1/6):43-47.
• [4]Sohi M H,Ebrahimi M,Ghasemi H M,et al.Microstructural study of surface melted and chromium surface alloyed ductile iron[J].Applied Surface Science,2012,258(19):7348-7353.
• [5]Filipovic M,Kamberovic Z,Korac M,et al.Correlation of microstructure with the wear resistance and fracture toughness of white cast iron alloys[J].Metals and Materials International,2013,19(3):473-481.
• [6]Zhi X H,Liu J Z,Xing J D,et al.Effect of cerium modification on microstructure and properties of hypereutectic high chromium cast iron[J].Materials Science and Engineering A,2014,603:98-103.
• [7]Reda R,Nofal A A,Ibrahim K M,et al.Microstructure-wear performance relationship of hypoeutectic 15%Cr-2%Mo white iron[J].International Journal of Materials Research,2012,103(7):838-846.
• [8]Lv Y,Sun Y,Zhao J,et al.Effect of tungsten on microstructure and properties of high chromium cast iron[J].Materials&Design,2012,39:303-308.
• [9]陈继刚,周野飞,姜永文,等.稀土硅铁添加剂细化高铬铸铁堆焊合金[J].材料热处理学报,2014,35(3):35-39.CHEN Ji-gang,ZHOU Ye-fei,JIANG Yong-wen,et al.Investigation into refinement of RE-Si-Fe on high chromium[J].Transactions of Materials and Heat Treatment,2014,35(3):35-39.
• [10]Pinho K F,Boher C,Scandian C.Effect of molybdenum and chromium contents on sliding wear ofhigh-chromium white cast iron at high temperature[J].Lubrication Science,2013,25(2):153-162.
• [11]Ramírez J H,Colás R,Garza-Montes-de-Oca N F.Effect of tempering on the oxidation resistance of a work roll grade high-chromium white cast iron[J].Oxidation of Metals,2014,81(3/4):421-434.
• [12]Wang S,Song L,Qiao Y,et al.Effect of carbide orientation on impact-abrasive wear resistance of high-Cr iron used in shot blast machine[J].Tribology Letters,2014,50(3):439-448.
• [13]Almeida D L,Mello J D B,Camargo Severo de M M,et al.Correlation among abrasive wear tests[J].Lubrication Science,2013,25(2):173-177.
• [14]Gasan H,Erturk F.Effects of a destabilization heat treatment on the microstructure and abrasive wear behavior of high-chromium white cast iron investigated using different characterization techniques[J].Metallurgical and Materials Transactions A,2013,44(11):4993-5005.
• [15]Tang X H,Chung R,Pang C J,et al.Microstructure of high(45 wt.%)chromium cast irons and their resistances to wear and corrosion[J].Wear,2011,271(9/10):1426-1431.
• [16]Gurevich Y G.Wear-resistant coatings of white cast iron on powder steels[J].Powder Metallurgy and Metal Ceramics,2012,50(9/10):619-24.
• [17]Zhang Q,Jiang Z,Wei D.Adhesion at oxide layer/substrate interface during sliding wear[J].International Journal of Surface Science and Engineering,2012,6(4):270-295.
• [18]Huang Z F,Xing J D,Gao Y M,et al.Microstructure and properties of hypereutectic high chromium white cast iron prepared under pressure[J].Iron Making&Steel Making,2011,38(5):359-362.
• [19]陈忱.不锈钢/碳钢复合板的焊接工艺及接头组织性能研究[D].南京:南京航空航天大学,2012.CHEN Chen.Study on process and microstructure and properties of welding joints of stainless steel/steel composite plate[D].Nanjing:Nanjing University of Astronautics and Aeronautics,2012.
• [20]Guo G C,Xue S F,Yan H W,et al.Microstructure and wear properties of nickel-based surfacing deposited by plasma transferred arc welding[J].Surface and Coatings Technology,2013,228(S):S276-S282.
• [21]徐锦锋,唐桢,任永明,等.高铬铸铁芯焊条堆焊层组织分析[J].焊接学报,2012(8):57-59.XU Jin-feng,TANG Zhen,REN Yong-ming,et al.Analysis of high chromium cast iron core welding layer[J].Welding Journal,2012(8):57-59.
• [22]巴德玛,孟凡军,孙晓峰,等.堆焊层表面纳米晶层摩擦磨损性能研究[J].摩擦学学报,2012,32(2):120-26.BA De-ma,MENG Fan-jun,SUN Xiao-feng,et al.Friction and wear behaviors of nanocrystalline surface layer prepared on deposited layer[J].Tribology,2012,32(2):120-26.
• [23]邓进俊,邵红红,彭玉婷,等.热处理对高铬铸铁组织与耐磨性的影响[J].金属热处理,2013,38(3):82-85.DENG Jin-jun,SHAO Hong-hong,PENG Yut-ing,et al.Effects of heat treatment on microstructure and wear resistance of high chromium cast iron[J].Heat Treatment of Metals,2013,38(3):82-85.
• [24]Petrica M,Peinsitt T,Badisch E.Characterization of impact abrasive wear produced by different rocks[J].Key Engineering Materials,2014,604:47-50.
• [25]Chung R,Tang X,Li D,et al.Microstructure refinement of hypereutectic high Cr cast irons using hard carbide-forming elements for improved wear resistance[J].Wear,2013,301(1/2):695-706.

文章评论(Comment)：