刘烜,李丽娜,丁燕红,赵水生,龙毅,叶荣昌,常永勤

• 1:北京科技大学材料科学与工程学院
• 2:北京科技大学材料科学与工程学院
• 3:北京科技大学材料科学与工程学院
• 4:北京科技大学材料科学与工程学院

摘要(Abstract)：

在空气中通过单辊快淬法制备了Fe57.6Co14.4B19.2Si4.8Nb4金属玻璃,研究了该金属玻璃在保持非晶态下退火温度和保温时间对静态磁性能和交流低频下的损耗特性的影响。随着退火温度的升高,直流最大磁导率升高、矫顽力下降、电阻率增加,低频交流铁芯损耗也随着温度的升高而明显降低,在773K下保温30min得到最佳的直流性能和交流低频损耗性能。

关键词(KeyWords)： 铁基金属玻璃;软磁材料;退火;低频损耗

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金项目(50471094)

作者(Author): 刘烜,李丽娜,丁燕红,赵水生,龙毅,叶荣昌,常永勤

参考文献(References)：

• [1]Schwarz R B,Shen T D,Harms U,et al.Soft ferromagnetism in amorphous and nanocrystalline alloys[J].Journal of Magnetism and Magnetic Materials,2004,283:223-230.
• [2]Inoue A,Makino A,Mizushima T.Soft magnetic properties of Fe based amorphous thick sheets with large glass forming ability[J].Journal of AppliedPhysics,1997,81:4029-4031.
• [3]Mizushima T,Makino A,Inoue A.Influence of Si addition on thermal stability and soft magnetic properties for Fe-Al-Ga-P-C-B glassy alloys[J].Journal ofApplied Physics,1998,83:6329-6331.
• [4]Shen T D,Schwarz R B.Bulk ferromagnetic glasses prepared by flux melting and water quenching[J].Applied Physics Letter,1999,75:49-51.
• [5]Koshiba H,Inoue A,Makino A.Fe-based soft magnetic amorphous alloys with a wide supercooled liquid region[J].Journal of Applied Physics,1999,85:5136-5138.
• [6]Chiriac H,Lupu N.Bulk amorphous(Fe,Co,Ni)70(Zr,Nb,M)10B20(M=Ti,Ta or Mo)soft magnetic alloys[J].Journal of Magnetism and MagneticMaterials,2000,215-216:394-396.
• [7]Long Y,ZHANG Wei,WANG Xin-min,et al.Effect of transition metal subsititution on the glass-formation ability and magnetic properties of Fe62Co9.5Nd3Dy0.5B25glassy alloy[J].Journal of Applied Physics,2002,91:5227-5229.
• [8]Shen B,Inoue A,Chang C.Superhigh strength and good soft-magnetic properties of(Fe,Co)-B-Si-Nb bulk glassy alloys with high glass-forming ability[J].Applied Physics Letter,2004,85:4911-4913.
• [9]Bitoh T,Makino A,Inoue A.Origin of low coercivity of(Fe0.75B0.15Si0.10)100-xNbx(x=1-4)glassy alloys[J].Journal of Applied Physics,2006,99:08F102-3.
• [10]Inoue A,Shen B L,Chang C T.Super-high strength of over 4000 MPa for Fe-based bulk glassy alloys in[(Fe1-xCox)0.75B0.2Si0.05]96Nb4system[J].ActaMaterialia,2004,52:4093-4099.
• [11]Lovas A,Varga B,Kiss L F,et al.The evolution of soft magnetic properties and the related density change during amorphous-nanocrystalline transformation[J].Journal of Magnetism and Magnetic Materials,2003,254-255:489-491.
• [12]非晶、纳米晶软磁合金带材[S].GB/T 19345-2003.

文章评论(Comment)：