赵建吉,许晓静,谈成,张香丽,徐驰,陈洋

• 1:江苏大学先进制造与现代装备技术工程研究院

摘要(Abstract)：

采用光学显微镜(OM)、电子背散射衍射检验(EBSD)、X射线衍射仪显微分析(XRD)、拉伸性能测试,研究了强化固溶处理对7085铝合金组织与性能的影响,并分析了其强化机理。结果表明:与常规固溶相比,强化固溶处理使合金的强度显著提高,伸长率变化不大;经时效处理后的7085铝合金的屈服强度为471.8 MPa、抗拉强度为518.3 MPa、伸长率为14.7%;通过对强化机理的分析,强度的提高主要来自于析出沉淀相强化。

关键词(KeyWords)： 7085铝合金;强化固溶;微观组织;强化机理

Abstract:

Keywords:

基金项目(Foundation): 江苏省工业科技支撑计划项目(BE2008118);; 江苏大学优秀青年学术骨干培育专项基金(1211110001);; 江苏省高校研究生科研创新计划项目(KYXX_0031,SJLX_0460);; 江苏高校优势学科建设工程项目

作者(Author): 赵建吉,许晓静,谈成,张香丽,徐驰,陈洋

DOI: 10.13289/j.issn.1009-6264.2015.11.018

参考文献(References)：

• [1]CHEN Kang-hua,LIU Wei-hong,LIU Yun-zhong,et al.Effect of promotively-solutionizing heat treatment on the mechanical properties and fracture behavior of Al-Zn-Mg-Cu alloys[J].Acta Metallurgica Science,2001,37(1):29-33.
• [2]陈康华,刘红卫.强化固溶对Al-Zn-Mg-Cu合金力学性能和断裂行为的影响[J].金属学报,2001,37(1):29-33.CHEN Kang-hua,LIU Wei-hong.Effect of promotively-solutionizing heat treatment on the mechanical properties and fracture behavior of Al-Zn-Mg-Cu alloys[J].Acta Metallurgica Science,2001,37(1):29-33.
• [3]陈康华,刘允中,刘红卫.7075和2024铝合金的固溶组织与力学性能[J].中国有色金属学报,2000,10(6):819-822.CHEN Kang-hua,LIU Yun-zhong,LIU Hong-wei.Microstructure and mechanical properties of enhanced solution treated 7075 and 2024 aluminum alloys[J].The Chinese Journal of Nonferrous Metals,2000,10(6):819-822.
• [4]陈康华,刘红卫,刘允中.强化固溶对7055铝合金力学性能和断裂行为的影响[J].中南工业大学学报,2000,31(6):528-531.CHEN Kang-hua,LIU Hong-wei,LIU Yun-zhong.Effect of enhanced solid solution on mechanical properties and fracture behavior of 7055 aluminum alloy[J].Journal of Central South University of Technology,2000,31(6):528-531.
• [5]陈晓明,宋仁国,李红霞,等.7075铝合金“双峰”时效研究[J].材料热处理学报,2010,31(2):80-84.CHEN Xiao-ming,SONG Ren-guo,LI Hong-xia,et al.Study on double-peak aging in 7075 aluminum alloy[J].Transactions of Materials and Heat Treatment,2010,31(2):80-84.
• [6]ZHAO Y H,LIAO X Z,JIN Z,et al.Microstructures and mechanical properties of ultrafine grained 7075 Al alloy processed by ECAP and their evolutions during annealing[J].Acta Materialia,2004,52(15):4589-4599.
• [7]Marcello C.Microstructure strengthening mechanisms in different equal channel angular pressed aluminum alloys[J].Materials Science and Engineering A,2013,560:413-432.
• [8]Luo P,Mc Donald D T,Xu W,et al.A modified Hall-Petch relationship in ultrafine-grained titanium recycled from chips by equal channel angular pressing[J].Scripta Materialia,2012,66(10):785-788.
• [9]Cabibbo M.Microstructure strengthening mechanisms in different equal channel angular pressed aluminum alloys[J].Materials Science and Engineering A,2013,560:413-432.
• [10]Dixit M,Mishra R S,Sankaran K K.Structure-property correlations in Al 7050 and Al 7055 high-strength aluminum alloys[J].Materials Science and Engineering A,2008,478(1):163-172.
• [11]Myhr O R,Grong,Andersen S J.Modelling of the age hardening behaviour of Al-Mg-Si alloys[J].Acta Materialia,2001,49(1):65-75.
• [12]Scattergood R O,Koch C C,Murty K L,et al.Strengthening mechanisms in nanocrystalline alloys[J].Materials Science and Engineering A,2008,493(1):3-11.

文章评论(Comment)：