摘要(Abstract)：

利用磁控溅射技术在铸造Ni-16Co-26Cr-10Al合金上溅射了相同成分的纳米晶涂层,并进行900℃热腐蚀实验,结果表明:溅射Ni-16Co-26Cr-10Al纳米晶涂层由于晶粒尺寸细小,促进了保护性氧化物形成元素Al沿原"短路扩散通道-晶界"向氧化前沿的扩散,从而促进了保护性Al2O3的快速形成,使得溅射Ni-16Co-26Cr-10Al纳米晶涂层表现出比M38合金更优异的抗热腐蚀性能。

关键词(KeyWords)： 热腐蚀;镍基高温合金;磁控溅射

Abstract:

Keywords:

基金项目(Foundation): 黑龙江省教育厅科技项目(No.11531319);; 黑龙江科技学院引进人才项目(06-13)

作者(Author): 孙俭锋,刘修超,周月波,王永东,陈洪玉

参考文献(References)：

• [1]Huang L,Sun XF,Guan HR,et al.Oxidation behavior of the directionally solidified Ni-base superalloy DS951 in air[J].Oxidation of Metals,2005,64(5/6):303-318.
• [2]Yuan F H,Han E H,Jo C Y,et al.The effect of crystallographic orientation on the oxidation behavior of a single-crystal nickel-base superalloy[J].Oxidation of Metals,2003,60(3/4):211-224.
• [3]Li MH,Sun XF,Li J G,et al.Oxidation behavior of a single-crystal Ni-base superalloyin air.I:at 800 and 900℃[J].Oxidation of Metals,2003,59(5/6):591-604.
• [4]Huang L,Sun XF,Guan HR,et al.Oxidation behavior of the single-crystal Ni-base superalloy DD32 in air at 900,1000,and 1100℃[J].Oxidation ofMetals,2006,65(5/6):391-408.
• [5]Lou H,Wang F,Zhu S,et al.Oxide formation of K38 superalloy andits sputtered micrograined coating[J].Surface and Coatings Technology,1994,63:105-114.
• [6]Goebel J A,Pettit F S.Na2SO4-induced accelerated oxidation of nickel[J].Met Trans,1970,1:1943-1954.
• [7]Goebel J A,Pettit F S,Goward G W.Mechanisms for the hot corrosion of nickel-based alloy[J].Met Trans,1973,4:261-278.
• [8]耿树江,王福会,朱圣龙.溅射IN738纳米晶涂层的涂盐热腐蚀行为[J].腐蚀科学与防护技术,2001,13(z1):405-407.
• [9]Li MH,Sun XF,Hu WY,et al.Hot corrosionof a single crystal-Ni-basedsuperalloy by Na-salts at 900℃[J].Oxidationof Metals,2006,65(1/2):137-150.
• [10]Wagner C.Type of reaction onthe oxidation of alloys[J].Z Elektroch,1959,63:772-782.
• [11]Peng X,Wang F.Morphologic investigation and growth of the alumina scale on magnetron-sputtered CoCrAl NCs with and without yttrium[J].CorrosionScience,2003,45(10):2293-2306.
• [12]Liu Z,Gao W,DahmK,et al.The effect of coating grain size onthe selective oxidation behavior of Ni-Cr-Al alloy[J].Script Materialia,1997,37:1551-1558.
• [13]Wang F.The effect of nanocrystallization onthe selective oxidation and adhesion of Al2O3scales[J].Oxidation of Metals,1997,48:215-224.
• [14]Guo MH,Wang QM,Ke PL,et al.The preparation and hot corrosionresistance of gradient NiCoCrAlYSiBcoatings[J].Surface and Coatings Technology,2006,200:3942-3949.
• [15]Guo MH,Wang Q M,GongJ,et al.Oxidation and hot corrosion behavior of gradient NiCoCrAlYSiBcoatings deposited by a combination of arc ion platingand magnetron sputteringtechniques[J].Corrosion Science,2006,48:2750-2764.
• [16]Peng X,Yan J,Zhou Y,et al.Effect of grainrefinement onthe resistance of 304 stailless steel to breakawayoxidationin wet air[J].Acta Materialia,2005,53:5079-5088.
• [17]Zhou Y,Peng X,Wang F.Cyclic oxidation of alumina-forming Ni-Al nanocomposites with and without CeO2addition[J].Script Materialia,2006,55:1039-1042.

文章评论(Comment)：