伍永刚,周正,杨奔,王莉馨,刘庆

• 1:重庆大学材料科学与工程学院

摘要(Abstract)：

定量表征珠光体钢丝在大应变量拉拔过程中珠光体片层间距的变化规律,对掌握超高强珠光体钢丝的组织与性能关系以及强韧化机理具有重要意义。本文工作根据珠光体钢丝组织变化特点,研究了72A珠光体钢丝在累计应变量3.58范围内的片层组织表征方法,在低应变量(ε<1.75)时,采用SEM图像观察,用圆周测量法统计测量了珠光体片层间距的变化;在高应变量(ε≥1.75)时,采用FIB制备TEM样观察,用线性截距法统计测量了珠光体片层间距的变化。结果表明,72A珠光体钢丝的珠光体片层间距由最初的81 nm左右减小到最终的17 nm左右。分析了72A珠光体钢丝的组织与性能关系,为研究珠光体钢丝拉拔过程中的变形及强化机理奠定了基础。

关键词(KeyWords)： 珠光体钢丝;冷拔;片层间距;组织;表征

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 伍永刚,周正,杨奔,王莉馨,刘庆

DOI: 10.13289/j.issn.1009-6264.2015.06.031

参考文献(References)：

• [1]GUO Ning,LUAN Bai-feng,LIU Qing.Influence of pre-torsion deformation on microstructures and properties of cold drawing pearlitic steel wires[J].Materials and Design,2013,50:285-297.
• [2]Tarui T,Maruyama N,Takahashi J,et al.Microstructure control and strengthening of high carbon steel wires[R].Nippon Steel Technical Report,2005:56-61.
• [3]Fang F,Zhao Y F,Zhou L C,et al.Texture inheritance of cold drawn pearlite steel wires after austenitization[J].Materials Science and Engineering A,2014,618:505-510.
• [4]Goto S,Kirchheim R,Al-Kassab T,et al.Application of cold drawn lamellar microstructure for developing ultra-high strength wires[J].Transactions of Nonferrous Metals Society of China,2007,17(6):1129-1138.
• [5]石祥虎,陈豫增,张昆华,等.高强度冷拔纳米珠光体钢丝的力学性能热稳定性[J].材料热处理学报,2013,34(S2):58-62.SHI Xiang-hu,CHEN Yu-zeng,ZHANG Kun-hua,et al.Thermal stability of mechanical properties of a high strength cold-drawn pearlitic steel wire[J].Transactions of Materials and Heat Treatment,2013,34(S2):58-62.
• [6]Elwazri A M,Wanjara P,Yue S.The effect of microstructural characteristics of pearlite on the mechanical properties of hypereutectoid steel[J].Materials Science and Engineering A,2005,404(1):91-98.
• [7]Zhang C L,Liu X,Zhou L Y,et al.Influence of pearlite interlamellar spacing on strain hardening behaviour in spring steel 60Si2Mn A[J].Procedia Engineering,2014,81:1283-1287.
• [8]张必明,赵宇飞,胡显军,等.冷拉SAE1008低碳钢丝强化机制的探讨[J].材料热处理学报,2014,35(1):115-119.ZHANG Bi-ming,ZHAO Yu-fei,HU Xian-jun,et al.Strengthening mechanism of a low carbon SAE1008 steel wire during cold drawing[J].Transactions of Materials and Heat Treatment,2014,35(1):115-119.
• [9]Vander Voort G F,Roosz A.Measurement of the interlamellar spacing of pearlite[J].Metallography,1984,17(1):1-17.
• [10]Ridley N.A review of the data on the interlamellar spacing of pearlite[J].Metallurgical Transactions A,1984,15(6):1019-1036.
• [11]栾佰峰,张达,郭宁,等.桥梁缆索用过共析钢热轧盘条微观组织定量表征[J].材料热处理学报,2011,32(7):78-82.LUAN Bai-feng,ZHANG Da,GUO Ning,et al.Quantitative characterization on microstructure of hot rolled hypereutectoid steel wire rod for bridge cable[J].Transactions of Materials and Heat Treatment,2011,32(7):78-82.
• [12]Hu X,Van Houtte P,Liebeherr M,et al.Modeling work hardening of pearlitic steels by phenomenological and Taylor-type micromechanical models[J].Acta Materialia,2006,54(4):1029-1040.
• [13]Nam W J,Bae C M,Oh S J,et al.Effect of interlamellar spacing on cementite dissolution during wire drawing of pearlitic steel wires[J].Scripta Materialia,2000,42(5):457-463.
• [14]Langford G.Deformation of pearlite[J].Metallurgical Transactions A,1977,8(6):861-875.
• [15]Nishida S,Yoshie A,Imagumbai M.Work hardening of hypereutectoid and eutectoid steels during drawing[J].ISIJ International,1998,38(2):177-186.
• [16]肖强,王伯健,刘世峰,等.剧烈塑性变形珠光体钢丝退火组织与性能[J].金属热处理,2013,38(6):6-8.XIAO Qiang,WANG Bo-jian,LIU Shi-feng,et al.Microstructure and properties of annealed pearlitic steel wire prepared by severe plastic deformation[J].Heat Treatment of Metals,2013,38(6):6-8.

文章评论(Comment)：