对粉末冶金法制备的纯Mo及Mo-43wt%Re合金不同状态下的力学性能和显微组织变化研究,结果表明:Mo-43wt%Re合金较纯Mo加工硬化显著,冷轧态纯Mo硬度仅为340HV,而Mo-43wt%Re合金的硬度达420HV。同时,Mo-43wt%Re合金抗高温软化性能较纯Mo得到显著提高,纯Mo的再结晶开始温度为900℃左右,Mo-43wt%Re合金在1350~1400℃开始再结晶,且再结晶晶粒细小,此时合金硬度较低,冷加工性能较好,可进行的最大变形量达50%。冷轧态Mo-43wt%Re合金出现大量位错胞组织,随着退火温度的升高,位错密度不断降低,且在不同温度下分别出现了均匀的螺位错网络和波浪形位错等组织。

关键词(KeyWords)： 钼铼合金;冷轧;退火;回复;再结晶

Abstract:

Keywords:

基金项目(Foundation): 国家高新技术发展“863”计划资助项目(2006AA03Z517);; 湖南省自然科学基金(05JJ30095)

作者(Author): 陈畅,汪明朴,郭明星,谭望,张真

参考文献(References)：

• [1]Geach G A,Hughes J E.The alloys of rhenium with molybdenum or with tungsten and having good high temperature properties[A].2ndPlansee Seminar,ed.Benesovsky F,London:Pergamon,1956.
• [2]Stephens J R,Witzke W R.Alloy softening in group via metals alloyed with rhenium[J].J Less-Common Met,1971,23:325.
• [3]Gypen L A,Deruyttere A.Multi-component intrinsic solid solution softening and hardening[J].J Less-Common Met,1977,56:91.
• [4]Todd L,Carlen J C,Martin B,et al.Investigation of mechanical properties and microstructure of various molybdenum-rhenium alloys[A].Space Technologyand Applications International Forum[C].1999:685.
• [5]Mannheim R L,Garin J L.Strain hardening of rhenium and two typical molybdenum-rhenium alloys manufactured by powder sintering[J].Z Metallkd,2000,91:848.
• [6]Wright N.A study of various contributions to substructural strengthening in Mo-33Re rolled to large strains[J].Materials Science and Engineering A,1988,104:85.
• [7]Mahajan S.Observations on the interaction of twins with grain boundaries in Mo-35at%Re alloy[J].Acta Metal,1973,21:255.
• [8]Davidson D L,Brotzen F R.Plastic deformation of molybdenum-rhenium alloy crystals[J].Acta Metall,1970,18:463.
• [9]Agnew S R,Leonhardt T.The low-temperature mechanical behavior of molybdenum-rhenium[J].JOM,2003,55(10):25.
• [10]Carlen J C,Bryskin B D.Concerning sigma-phase in molybdenum-rhenium alloys[J].Journal of Materials Engineering and Performance,1994,3(2):282.

文章评论(Comment)：