孙良省,许晓静,蒋伟,范亚洲

• 1:江苏大学先进制造与现代装备技术工程研究院

摘要(Abstract)：

采用X射线衍射分析(XRD)、电子背散射衍射分析(EBSD)、电导率测试、硬度测试、拉伸试验、晶间腐蚀试验和剥落腐蚀试验,研究了固溶处理前的预回复处理(250℃×24 h+300℃×6 h+350℃×6 h+400℃×6 h)对高合金化铝合金Al-13.0Zn-3.16Mg-2.8Cu-0.2Zr-0.07Sr挤压材在T652态组织与性能的影响。结果表明,固溶前的预回复处理降低了位错密度,减小了平均晶粒尺寸(8.764μm vs.4.835μm)和平均晶界角度,显著提高了低角度晶界数目分数(0.410 vs.0.658)和电导率(24.6%ICAS vs.26.3%ICAS),降低了硬度(228.2 HV vs.227.0 HV)、屈服强度(680.3 MPa vs.662.5 MPa)、抗拉强度(714.5 MPa vs.695.5 MPa)和伸长率(7.6%vs.5.6%),提高了抗晶间腐蚀和抗剥落腐蚀性能;定量分析显示,预回复处理轻微降低了合金位错强化、低角度晶界强化和高角度晶界强化的总强化,合金强度的降低主要归因于合金固溶强化和时效沉淀析出相强化的总强化的降低;抗腐蚀性能的提高可以归因于合金低角度晶界数目百分比的提高。

关键词(KeyWords)： Al-Zn-Mg-Cu铝合金;预回复处理;强化机理;组织性能

Abstract:

Keywords:

基金项目(Foundation): 江苏省工业科技支撑计划项目(BE2008118);; 江苏大学“拔尖人才培养工程基金”(1211110001);; 江苏省高校研究生科研创新计划项目(CXLX12_0620);; 江苏省优势学科资助

作者(Author): 孙良省,许晓静,蒋伟,范亚洲

DOI: 10.13289/j.issn.1009-6264.2015.12.011

参考文献(References)：

• [1]Morere B,Maurice C,Driver J H,et al.Microstructural characterization of a 7010 alloy after hot deformation and solution treatment[J].Materials Science Forum,1996(217/222):517-522.
• [2]Deng Y L,Wan L,Zhang Y,et al.Evolution of microstructures and textures of 7050 Al alloy hot-rolled plate during staged solution heat-treatments[J].Journal of Alloys and Compounds,2010,498(1):88-94.
• [3]许晓静,张允康,邓平安,等.预回复退火对7085铝合金挤压材组织和性能的影响[J].材料热处理学报,2014,35(8):36-40.XU Xiao-jing,ZHANG Yun-kang,DENG Ping-an,et al.Effect of pre-recovery-annealing treatment on microstructure and properties of extruded 7085aluminum alloy[J].Transactions of Materials and Heat Treatment,2014,35(8):36-40.
• [4]Youssef K M,Scattergood R O,Murty K L,et al.Nanocrystalline Al-Mg alloy with ultrahigh strength and good ductility[J].Scripta Materialia,2006,54(2):251-256.
• [5]Xu X J,Cao J Q,Cheng X N,et al.Tensile properties of 2024 Al alloy processed by enhanced solid-solution and equal-channel angular pressing[J].Transactions of Nonferrous Metals Society of China,2006,16(S3):1541-1544.
• [6]Xu X,Shao H,Gao J,et al.Effect of Si C film on tensile properties of nanostructured Ti produced by compressive deformation at liquid-nitrogen temperature[J].Materials Science and Engineering A,2008,493(1):195-201.
• [7]Zhao Y H,Liao X Z,Jin Z,et al.Microstructures and mechanical properties of ultrafine grained 7075 Al alloy processed by ECAP and their evolutions during annealing[J].Acta Materialia,2004,52(15):4589-4599.
• [8]Cabibbo M.Microstructure strengthening mechanisms in different equal channel angular pressed aluminum alloys[J].Materials Science and Engineering A,2013,560:413-432.
• [9]Luo P,Mc Donald D T,Xu W,et al.A modified Hall-Petch relationship in ultrafine-grained titanium recycled from chips by equal channel angular pressing[J].Scripta Materialia,2012,66(10):785-788.
• [10]Dixit M,Mishra R S,Sankaran K K.Structure-property correlations in Al 7050 and Al 7055 high-strength aluminum alloys[J].Materials Science and Engineering A,2008,478(1/2):163-172.
• [11]Scattergood R O,Koch C C,Murty K L,et al.Strengthening mechanisms in nanocrystalline alloys[J].Materials Science and Engineering A,2008,493(1/2):3-11.

文章评论(Comment)：