吴保平,李林翰,吴剑涛,王祯,董建新,李俊涛

• 1:北京科技大学材料科学与工程学院
• 2:钢铁研究总院高温材料研究所

摘要(Abstract)：

研究了4种固溶温度:1000、1040和1080和1120℃×4 h,AC(空冷)+双时效(845℃×24 h/AC+760℃×16 h/AC)热处理制度对铸造waspaloy合金组织的影响。结果表明,铸态waspaloy合金组织由γ基体、团状γ'相和MC碳化物组成。固溶处理后,铸态γ'相溶解到基体中,并随固溶温度升高,铸态γ'相含量逐渐减少。当固溶温度大于1080℃时,枝晶形貌消失,铸态γ'相完全溶解;在随后845℃稳定化处理过程中,均匀细小的二次γ'相开始析出,MC碳化物开始分解,并在晶界处析出不连续的粒状M23C6碳化物;经过760℃时效处理后,更多均匀细小的二次γ'相析出并长大。最终确定铸造waspaloy合金的最佳固溶温度应大于1080℃,此时经时效后组织更加均匀一致。

关键词(KeyWords)： waspaloy合金;固溶处理;显微组织

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 吴保平,李林翰,吴剑涛,王祯,董建新,李俊涛

DOI: 10.13289/j.issn.1009-6264.2014.s1.027

参考文献(References)：

• [1]冶军.美国镍基高温合金[M].北京:科学出版社,1978.
• [2]Penkalla H J,Wosik J,Czyrska-Filemonowicz A.Quantitative microstructural characterization of Ni-base superalloys[J].Materials Chemistry and Physics,2003,81(2-3):417-423.
• [3]Wei X.Experimental study on the machining of a shaped hole in Ni-based super-heat-resistant alloy[J].Journal of Materials Processing Technology,2002,129(1-3):143-147.
• [4]Cao W D,Kennedy R L.New developments in wrought 718-type superalloys[J].Acta Metallugica Sinica(English letters),2005,18(1):39-46.
• [5]董建新,张麦仓,郑磊,等.组织特征对GH864合金裂纹扩展行为的影响[J].中外能源,2008,13(增刊1):24-29.DONG Jian-xin,ZHANG Mai-cang,ZHENG Lei,et al.A study on influence of microstructure on crack propagation of GH864 alloy[J].Sino-Global Energy,2008,13(S1):24-29.
• [6]中国航空材料手册.变形高温合金铸造高温合金[M].北京:中国标准出版社,2001.
• [7]张玉峰,吴天平,方文,等.不同热处理工艺下GH864合金的组织性能分析[J].中外能源,2008,18(增刊1):30-33.ZHANG Yu-feng,WU Tian-ping,FANG Wen,et al.An analysis of the structural properties of GH864 alloy in different heat processing processes[J].Sino-Global Energy,2008,18(S1):30-33.
• [8]姚志浩,董建新,张麦仓,等.GH864合金显微组织与力学性能的关联性[J].稀有金属材料与工程,2010,39(9):1565-1570.YAO Zhi-hao,DONG Jian-xin,ZHANG Mai-cang,et al.Relationship between microstructures and properties for GH864 superalloy[J].Rare Metal Materials and Engineering,2010,39(9):1565-1570.
• [9]王迪,陈国良.烟气轮机用合金叶片热处理工艺的选择[J].北京科技大学学报,1993,15(1):20-24.WANG Di,CHEN Guo-liang.Selection of heat treatments for waspaloy alloy as flue gas turbine blade[J].Journal of University of Science and Technology Beijing,1993,15(1):20-24.
• [10]姚志浩,董建新,张麦仓,等.固溶温度对GH864合金组织性能的影响[J].材料热处理学报,2011,32(7):44-50.YAO Zhi-hao,DONG Jian-xin,ZHANG Mai-cang,et al.Effect of solution temperature on microstructure and properties of GH864 alloy[J].Transactions of Materials and Heat Treatment,2011,32(7):44-50.
• [11]Malow T,ZHU Jia-wei,Rajeshwar Prasad Wahi.Influence of heat treatment on the microstructure of the single-crystal nickel-base superalloy SC16[J].Journal of Metallurgy,1994,85(1):9-19.
• [12]HUANG Yan,WANG Lei,LIU Yang,et al.Microstructure evolution of a new directionally solidified Ni-based superalloy after long-term aging at950°C upto 1000 h[J].Transactions of Nonferrous Metals Society of China,2011,21(10):2199-2204.
• [13]冯瑞.金属物理[M].北京:科学技术出版社,1988.
• [14]Garosshen T J,Mccarthy G P.Low temperature carbide precipitation in a nickel base superalloy[J].Metallurgical Transactions A,1985,16(7):1213-1223.
• [15]Wei C N,Bor H Y,Chang L.The influence of carbon addition on carbide characteristics and mechanical properties of CM-681LC superalloy using fine grain process[J].Journal of Alloys and Compounds,2011,509(18):5708-5714.
• [16]Jena A K,Chaturvedi M C.The role of alloying elements in the design of nickel base superalloys[J].Journal of Materials Science,1984,19(10):3132-3139.
• [17]Turnbull D.Kinetics of heterogeneous nucleation[J].Journal of Chemical Physics,1950,18(2):198-203.

文章评论(Comment)：