摘要(Abstract)：

选择新型细晶高强IF钢为研究对象,在实验室进行了热轧、冷轧及罩式退火实验。利用光学显微镜、透射电镜复型和电子背散射衍射(EBSD)技术,研究了不同退火时间对细晶高强IF钢显微组织、析出相及织构的影响。结果表明,选择合适的退火时间,晶粒变得细小、均匀。细晶高强IF钢在退火过程中析出大量的Nb C、Nb(CN)相;随退火时间延长,钢中析出相粒子偏聚长大。为了获得较强的有利织构及优异的冲压性能,实验钢退火时间应选定在5 min。

关键词(KeyWords)： 细晶高强IF钢;退火时间;析出相;织构

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金(51474127)

作者(Author): 陈越,张红梅,孙成钱,王洪斌,马多,郭雅楠,贾宏斌

DOI: 10.13289/j.issn.1009-6264.2015.04.024

参考文献(References)：

• [1]康永林.现代汽车板工艺及成形理论与技术[M].北京:冶金工业出版社,2009.
• [2]李守华,李俊.汽车用高强度IF钢的研究进展[J].上海金属,2007,9(5):66-70.LI Shou-hua,LI Jun.Research progress of automotive high strength IF steel[J].Shanghai Metal,2007,9(5):66-70.
• [3]王利,杨雄飞,陆匠心.汽车轻量化用高强度钢板的发展[J].钢铁,2006,9(9):1-8.WANG Li,YANG Xiong-fei,LU Jiang-xin.Development of high strength steel sheets for automobile lightweight[J].Iron and Steel,2006,9(9):1-8.
• [4]Takashi S,Shuji K,Sadao H,et al.Materials and technologies for automotive use[J].JFE Technical Report,2003,11(2):1-16.
• [5]Urabe T,Fujit a T,Yamazak i Y J.Development of high strength steel with fine grain structure f or exposure panel[J].JFE Technical Report,2001,10(55):13-18.
• [6]Kitano F.New type of IF high strength steel with superior ant i-secondary work embrittlement[J].Transaction ISIJ,2001,11(41):1402-1405.
• [7]Takeshi F T,Toshiaki U,Michitaka S.High performance high strength steel sheets for exposed auto body panels[J].JFE Technical Report,2007,12(1):8-11.
• [8]Wang X L,Wei Y H,Wang W.Calculation of second phase particle-grain boundary interaction range[J].Acta Metallurgica Sinica,2008,21(1):8-14.
• [9]Zurob H S,Brechet Y,Purdy G.A model for the competition of precipitation and recrystallization in deformed austenite original research article[J].Acta Materialia,,2001,49(20):4183-4190.
• [10]Zhang Z H,Liu Y N,Liang X K.The effect of Nb on recrystallization behavior of a Nb microalloyed steel[J].Materials Science and Engineering A,2008,474(1/2):254-260.
• [11]雍岐龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006.
• [12]Jeong W C.Effect of hot-rolling temperature on microstructure and texture of an ultra-low carbon Ti-interstitial-free steel[J].Materials Letters,2008,62(1):91-94.

文章评论(Comment)：