魏凤玉,胡芳,黄登銮

• 1:合肥工业大学化工学院

摘要(Abstract)：

研究了螺纹钢在经冷却剂CQ、水或空气冷却后的耐蚀性能。室外大气暴露实验和干湿交替循环加速腐蚀实验表明,采用试剂CQ冷却的螺纹钢耐蚀性能明显优于水和空气冷却的。XRD、SEM和TPR结果表明,冷却剂对螺纹钢大气腐蚀产物的物相组成无影响,但影响其相对含量,从而改变锈层保护性系数。水冷、空冷和CQ冷螺纹钢的锈层保护性系数分别为0.23、0.27和0.43。因此,试剂CQ冷却的螺纹钢在大气腐蚀过程中生成了相对稳定致密的锈层,从而减缓了腐蚀反应的进行,对螺纹钢起一定的保护作用。

关键词(KeyWords)： 螺纹钢;耐腐蚀性;冷却剂;保护性系数

Abstract:

Keywords:

基金项目(Foundation): 合肥工业大学生创新基金(cxsy10062)

作者(Author): 魏凤玉,胡芳,黄登銮

DOI: 10.13289/j.issn.1009-6264.2011.12.030

参考文献(References)：

• [1]Zaky A I,El-Morsy A,El-Bitar T.Effect of different cooling rates on thermomechanically processed high-strength rebar steel[J].Materials ProcessingTechnology,2009,209(3):1565-1569.
• [2]许铁群,刘宏伟,严川伟,等.穿水钢筋锈蚀与防护的研究与应用[J].材料保护,2008,41(增刊):233-234.XU Tie-qun,LIU Hong-wei,YAN Chuan-wei,et al.Study and application of the rust and protection of the water-cooling bars[J].Materials Protection,2008,41(Supplement):233-234.
• [3]Novak P,Mala R,Joska L.Influence of pre-rusting on steel in concrete[J].Cement and Concrete Research,2001,31(4):589-593.
• [4]魏洁,董俊华,柯伟.新型化学剂快速冷却热轧螺纹钢的防锈性能研究[J].腐蚀科学与防护技术,2009,21(5):468-471.WEI Jie,DONG Jun-hua,KE Wei.Corrosion resistance of hot rolled rebar quenched with a new chemical reagent[J].Corrosion Science andProtection Technology,2009,21(5):468-471.
• [5]采油采气专业标准化委员会.SY/T 5273-2000中国标准书号[S].北京:中国标准出版社.2000.
• [6]Ahamad I,Quraishi M A.Bis(benzimidazol-2-yl)disulphide:An efficient water soluble inhibitor for corrosion of mild steel in acid media[J].Corrosion Science,2009,51(9):2006-2013.
• [7]Fuente D de la,Díaz I,Simancas J,et al.Long-term atmospheric corrosion of mild steel[J].Corrosion Science,2011,53(2):604-617.
• [8]Castao J G,Botero C A,Restrepo A H,et al.Atmospheric corrosion of carbon steel in Colombia[J].Corrosion Science,2010,52(1):216-223.
• [9]Monnier J,Neff D,Réguer S,et al.A corrosion study of the ferrous medieval reinforcement of the Amiens cathedral.Phase characterisation andlocalisation by various microprobes techniques[J].Corrosion Science,2010,52(3):695-710.
• [10]Pineau A,Kanari N,Gaballah I.Kinetics of reduction of iron oxides by H2 Part I:Low temperature reduction of hematite[J].Thermochimica Acta,2006,447(1):89-100.
• [11]Pinna F,Fantinel T,Strukul G,et al.TPR and XRD study of ammonia synthesis catalysts[J].Applied Catalysis A:General,1997,149(2):341-351.
• [12]Yamashita M,Miyuki H,Matsuda Y,et al.The long term growth of the protective rust layer formed on weathering steel by atmospheric corrosion duringa quarter of a century[J].Corrosion Science,1994,36(2):283-299.
• [13]Dillmann Ph,Mazaudier F,HrléS.Advances in understanding atmospheric corrosion of iron.I.Rust characterisation of ancient ferrous artefactsexposed to indoor atmospheric corrosion[J].Corrosion Science,2004,46(6):1401-1429.
• [14]杨景红,刘清友,王向东,等.耐候钢及其腐蚀产物的研究概况[J].中国腐蚀与防护学报,2007,27(6):367-372.YANG Jing-hong,LIU Qing-you,WANG Xiang-dong,et al.The progress of investigation on weathering steel and its rust layer[J].Journal of ChineseSociety for Corrosion and Protection,2007,27(6):367-372.
• [15]张全成.大气腐蚀过程中耐候钢表面保护性锈层的表征及其改性研究[D].上海:上海交通大学,2002.

文章评论(Comment)：